Default COE as it relates to temperature and viscosity

I have a few questions about glass COE/Temperature/Viscosity ...

Does LOWER COE mean ...
LOWER Viscosity (moves slower)
and Higher (or LOWER) temperature to work with?

I am sorry if this has been asked 1,000's of times here before.
(This is my first post ... and have not found the "search function yet")

Thank You
Reply With Quote
  #2  
Old 2019-08-26, 10:02am
Robin Passovoy Robin Passovoy is offline
Senior Member
 
Join Date: Dec 31, 2009
Posts: 495
Default

COE stands for Coefficient of Expansion, and it's a measure of the hardness of the glass. The lower the COE, the less it expands or contracts, and the harder it is.
The higher the COE, the softer it is, and the more it expands or contracts.
Softer glass, such as 104 or 133 (soda lime and Satake glass) therefore melts faster and is runnier. Harder glass such as 90, 96, and 33 (Bullseye, Spectrum, and borosilicate) is much stiffer. All require different annealing temperatures that can vary somewhat if you're using regular or silver glass.
Most people start with softer glass, with 104 being the favorite, since the color range and ease of availability is the greatest, and it's easy to work.
Reply With Quote
  #3  
Old 2019-08-26, 4:42pm
Speedslug's Avatar
Speedslug Speedslug is offline
Phill
 
Join Date: Mar 21, 2009
Location: Winnebago, MN
Posts: 2,324
Default

I will add that transparent glass is often stiffer than opaque glass of the same class of coe.

With the exception of Double Helix brand clears like Zepher. It is very clear but it melts like butter.
__________________
We have to take care of ourselves so we can take care of each other.
Reply With Quote
  #4  
Old 2019-09-16, 2:08pm
5betsy 5betsy is offline
Senior Member
 
Join Date: Apr 17, 2009
Location: Olympia!
Posts: 347
Default

There have been a couple very thorough discussions of viscosity and Coe both here on LE and over on Wetcanvas. I find searching inside both sites frustrating so I use Google.

Try using search term 'lampworketc viscosity' and both threads pop up.
Reply With Quote
Reply


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 12:00pm.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2021, Jelsoft Enterprises Ltd.
Your IP: 3.237.97.64